MS Polymer® technology is widely recognized as the best choice of base resin for manufacturing sealants, adhesives and coatings.
OTHER APPLICATIONS
| Description Fast curing, elastic and high cohesion sealing adhesive, MS Polymer® based. Used for caulking joints structures and teak deck and for bonding. Med B – Med D Certifications. |
Characteristics Excellent adhesion to many substrates without the use of primer. Resistant to fresh and sea water, UV rays, aging, perfectly stable for caulking joints of teak artifacts and decks. No bubbles during catalysis. |
ELONGATION: 350% OPEN TIME: 15 min. HARDNESS: 40 Shore A |
| Description Fast curing, elastic and high cohesion sealing. Used for caulking joints of teak structures and teak deck. Med B – Med D Certifications. |
Characteristics Excellent adhesion to many substrates without the use of primer. Resistant to fresh and sea water, UV rays, aging, perfectly stable for caulking joints of teak artifacts and decks. No bubbles during catalysis. |
ELONGATION: 250% OPEN TIME: 25 min. HARDNESS: 32 Shore A |
| Description Fast curing, elastic and high cohesion MS Polymer® based sealing adhesive. Used for high performance bonding, sealing and elastic joints, also for outdoor use. Med B – Med D certifications. |
Characteristics Excellent adhesion to a wide variety of surfaces and different substrates such as aluminum, anodized aluminum, copper, glass, stainless steel, ABS and PVC; no primer on many unpainted metals and hardwoods such as mahogany and teak, also on polyurethane sealants and plastics. Paintable (non-silicone polymer chain). |
ELONGATION: 300% OPEN TIME: 7 min. HARDNESS: 55 Shore A |
| Description Fast curing, elastic and high cohesion MS Polymer® based sealing adhesive. Used for high performance bonding, sealing and elastic joints, also for outdoor use. |
Characteristics Excellent adhesion to painted and non-painted metals, plastic materials and acrylic composite agglomerates, stiff plastics, cement, ceramics, imitation stone, wood, glass. Paintable (non-silicone polymer chain). |
ELONGATION: 600% OPEN TIME: 30 min. HARDNESS: 22 Shore A |
| Description Transparent fast curing, elastic and high cohesion MS Polymer® based sealing adhesive. Used for high performance bonding, sealing, elastic adhesive joints also for outdoor use. |
Characteristics Excellent adhesion to a wide variety of surfaces such as aluminum, anodized aluminum, polyester and stainless steel. Excellent resistance to UV rays, humidity and atmospheric agents. |
ELONGATION: 225% OPEN TIME: 6 min. HARDNESS: 42 Shore A |
| Description Transparent fast curing, elastic and high cohesion MS Polymer® based sealing adhesive. Used for high performance bonding, sealing, elastic adhesive joints, used in the building industry for completely transparent bonding, also for outdoor use. |
Characteristics Excellent adhesion on painted and unpainted metals, plastics and acrylic solid surfaces, polyester GF, PA, PC, DKS, PVC, PMMA, cement, ceramics, stone design, wood, glass. Paintable (non-silicone polymer chain). Excellent resistance to UV rays, humidity and atmospheric agents. |
ELONGATION: 400% OPEN TIME: 5 min. HARDNESS: 40 Shore A |
| Description Transparent fast curing, elastic and high cohesion MS Polymer® based sealing adhesive. Used for high performance bonding, sealing, elastic adhesive joints also for outdoor use. Med B – Med D certifications. |
Characteristics Excellent adhesion on a wide variety of surfaces and different substrates such as aluminium, anodized aluminium, glass, stainless steel, ABS and PVC, on many unpainted metals and on hardwoods such as mahogany and teak, even on polyurethane sealants. Production of laminated composite panels, construction of sandwich panels. |
ELONGATION: 350% OPEN TIME: 20-30 min. HARDNESS: 27 Shore A |
| Description Fast curing, elastic and high cohesion MS Polymer® based sealing adhesive. Used for high performance bonding, sealing and elastic adhesive joints. |
Characteristics Excellent adhesion on painted and unpainted metals, plastics and solid surfaces, acrylics, polyester GF, PA, PC, S, DKS, PVC, PMMA, cement, ceramics, stone design, wood, glass. Paintable (non-silicone polymer chain). |
ELONGATION: 300% OPEN TIME: 15-20 min. HARDNESS: 45 Shore A |
| Description Transparent fast curing, elastic and high cohesion MS Polymer® based sealing adhesive. Used to realize bonding, sealing, elastic adhesive joints of high performance. |
Characteristics Excellent adhesion on painted and unpainted metals, plastics and solid surfaces acrylics, polyester GF, PA, PC, S, DKS, PVC, PMMA, cement, ceramics, stone design, wood, glass, back painted mirror, film and black-laquared glass. Paintable (non-silicone polymer chain). Withstands temperature peaks up to +200°C for about 30 minutes. |
ELONGATION: 300% OPEN TIME: 10-20 min. HARDNESS: 35 Shore A |
| Description Transparent fast curing, elastic and high cohesion MS Polymer® based sealing adhesive. Used to realize bonding, sealing, elastic adhesive joints of high performance. |
Characteristics Excellent adhesion to metals, natural stones, wood, hardwood, glass, laminates, channels, advertising signs. Excellent resistance in indoors and outdoors. |
ELONGATION: 470% OPEN TIME: 8 min. HARDNESS: 47 Shore A |
| Description Highly and permanently elastic and high cohesion MS Polymer® based sealing adhesive. |
Characteristics Excellent adhesion on plastic materials such as ABS, polycarbonates, PVC, PMMA, Corian® and nylon loaded with 30% glass. Suitable for gluing back-painted mirrors and with safety films, glass and lacquered glass. |
ELONGATION: 200% OPEN TIME: 15 min. HARDNESS: 65 Shore A |