Sealants are classified according to application and ability to adapt to joint movement, as well as load behavior dynamic, temperature resistance, type of application and chemical base.

OTHER APPLICATIONS

Description
Acetic silicone sealant with high modulus of elasticity suitable for sealing contact points and joints exposed to constantly high temperatures up to 300°C. 		Characteristics
Excellent resistance to UV rays, chemical agents, outdoor temperatures, rain and snow.
Excellent adherence on aluminum, metals in general, ceramics, glass, porcelain or enameled surfaces. 		ELONGATION: 150-300%
OPEN TIME: 10-20 amin.
HARDNESS: 20-30 aShore aA

Description
Neutral oxymic silicone sealant, permanently elastic.
Used for sealing joints of different materials.
It does not slip in vertical joints, can withstand 20% expansion.
Odorless and ideal for sealing even in closed environments. 		Characteristics
Excellent resistance to weather, UV rays, snow, rain.
Adheres to steel, aluminum, general metals, cement, ceramics, stone, wood, glass and most plastics. 		ELONGATION: 200-300%
OPEN TIME: 5-20 min.
HARDNESS: 15-25 Shore A

Colors


Joint (mm)

Considering the thickness of the joint (depth and width), the table shows the linear meters that can be achieved with a 300 ml cartridge.

Description
Transparent low modulus neutral alcoholic silicone sealant.
Used for sealing industrial joints, sanitary ware, building joints, for sanitary ware, suitable for installing windows and doors in general. 		Characteristics
Excellent resistance to atmospheric agents, UV rays and mould.
Excellent adhesion on alkaline substrates such as concrete, marble, fibrous cement, glass, tiles, ceramics, paints, glazed tiles, impregnated, painted wood and most plastics. 		ELONGATION: 300%
OPEN TIME: 35 min.
HARDNESS: 24 Shore A

Description
Single-component, fast-curing, odorless elastic sealant.
Color: matte black. 		Characteristics
Sealing of metal parts and motor plastics, resistant to high temperatures and contact with oils.
It maintains its elastic characteristics unchanged at temperatures between -40 and +250°C continuously and with peaks of +300°C.
Thanks to its specific formulation it maintains the chemical-physical characteristics unchanged after complete polymerization. 		ELONGATION: 130%
OPEN TIME: 15±3 min.
HARDNESS: 35 Shore A